| 性能项目 | 熔体流动速率 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 22 | g/10min |
| 比重 | 200℃×5kg | ASTM D-1238 | 1.8 | g/10min | |
| 弯曲强度 | ASTM D-792 | 1.05 | 23/23℃ | ||
| 机械性能 | 弯曲弹性率 | ASTM D-790 | 11200 | lb/in2 | |
| 引张强度 | ASTM D-790 | 3.8×105 | lb/in2 | ||
| 引张强度 | ASTM D-638 | 480 | kg/cm2 | ||
| IZOD冲击强度 | ASTM D-638 | 6800 | lb/in2 | ||
| 弯曲弹性率 | 1/8" | ASTM D-256 | 3.7 | ft.lb/in | |
| 弯曲强度 | ASTM D-790 | 2.7×104 | kg/cm2 | ||
| 洛氏硬度 | ASTM D-790 | 790 | kg/cm2 | ||
| IZOD冲击强度 | ASTM D-785 | 116 | R | ||
| IZOD冲击强度 | 1/4" | ASTM D-256 | 18 | kg.cm/cm | |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 3.3 | ft.lb/in | |
| 伸长率 | 1/8" | ASTM D-256 | 20 | kg.cm/cm | |
| 热变形温度 | ASTM D-638 | 20 | % | ||
| 热性能 | 维卡软化点 | ASTM D-648 | 88(190) | ℉ | |
| 燃烧性 | ASTM D-1525 | 105 | ℃ | ||
| 维卡软化点 | File No. E56070 UL&C-UL | 1/16"HB | |||
| 热变形温度 | ASTM D-1525 | 221 | ℉ | ||
| ASTM D-648 | 99(210) | ℃ |